ML 2319 AlCu6MnZrTi

Typical composition in %

Si <0,20
Fe <0,30
Cu 5,80 - 6,80
Mn 0,20 - 0,40
Mg <0,02
V 0,05 - 0,15
Zn <0,10
Zr 0,10 - 0,25
Be <0,0003
Ti 0,10 - 0,20
Others <0,05
Others, total <0,15

Classification

EN ISO 18273  :  S 2319 (AICu6MnZrTi)
Matériel Nr  :  2014, 2219 and 2519
AWS A 5-10  :  ER 2319

Base materials

See table

Remarks

This alloy is mainly used in the air and spacecraft industry. The copper content makes this alloy highly resistant.

Physical properties of pure weld metal (Approx. values)

0,2% Yield strength Rp0,2 [MPa]  :  180
Tensile strength Rm [MPa]  :  240
Elongation A5 ( L0=5d0 ) [%]  :  3
Test temperature [°C]  :  20

Welding position

PA, PB, PC, PF

Shielding gas

I1, I2, I3 (Argon, Helium or Argon/Helium-mixtures)

Polarity

MIG =+, TIG ~

Approvals

None

Dimensions Ø

MIG-wires  :  0,8 ;1,0 ; 1,2 ; 1,6 ; 2,0 ; 2,4
TIG-rods [mm]  :  1,6 ; 2,0 ; 2,4 ; 3,2 ; 4,0

Wire packagings

Spools  :  Packaging units

S 100 / 0,5 kg  :  20 spools = 10 kg (box)
S 200 / 2 kg  :  4  spools = 8 kg (box)
S 300 / 6 kg  :  84 spools = 504 kg (pallet)
B 300 / BS 300 / 7kg  :  84 spools = 588 kg (pallet)
B 400 / 18 kg  :  28 spools = 504 kg (pallet)
B 400 / 40 kg  :  15 spools = 600 kg (pallet)
Eco-drum / 80 kg  :   2 drums = 160 kg ou 320 kg (pallet)
Jumbo-drum / 140 kg  :  2 drums = 280 kg (pallet)

Rod packagings

Carton 5 kg ; carton 10 kg  :  Length 1.000 mm